| Recommended printing conditions | Nozzle Temperature260-280 °CRecommended Nozzle Diameter0.4-1.0 mmRecommended build surface treatmentPEI or Coating with PVP glueBuild plate temperature70-80 °CChamber TempSupports printing without sealingCooling fan speedOffPrint speed30-120 mm/sRetraction distance1-3 mmRetraction speed1800-3600 mm/minRecommended Support MaterialFusFree™ S-PAHT Quick-Remove SupportDrying setting80-100℃ for 4-6hAnnealing80-100℃ for 4-8h |
|---|
| | Nozzle Temperature260-280 °CRecommended Nozzle Diameter0.4-1.0 mmRecommended build surface treatmentPEI or Coating with PVP glueBuild plate temperature70-80 °CChamber TempSupports printing without sealingCooling fan speedOffPrint speed30-120 mm/sRetraction distance1-3 mmRetraction speed1800-3600 mm/minRecommended Support MaterialFusFree™ S-PAHT Quick-Remove SupportDrying setting80-100℃ for 4-6hAnnealing80-100℃ for 4-8h |
|---|
Printing Tips：Nylon material is very easy to absorb moisture within the environment, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately afteropening the FusForce™️ PAHT vacuum foil bag for printing. Please put the unused filament back into theoriginal aluminum foil bag for sealed storage.After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 80-100°C for 4-6h to restore the printing quality of FusForce™️ PAHT.It is recommended to use hardened steel and above grade nozzles made by Phaetus, which can effectively improve the print quality. Besides, it is recommended that the thickness of the heating block is longer 12mm.
No matching print profile files.
Synced from the linked Product Parameters V2 record — use as a starting point for slicing and test prints.
Core temperature, speed and cooling settings from Product Parameters V2.
Nozzle, build plate and pre-print preparation recommendations.
Support material, spacing and compatible material recommendations.
FusRock 3D printing materials in the Prototyping segment, illustrated by “Verification design of small work wheel rim”, balancing structural strength, print fidelity and field reliability.
FusRock 3D printing materials in the Automotive segment, illustrated by “Automobile oil pipeline inspection tools”, balancing structural strength, print fidelity and field reliability.
FusRock 3D printing materials in the Industrial Parts segment, illustrated by “Spare parts for industrial equipment connection”, balancing structural strength, print fidelity and field reliability.
FusRock 3D printing materials in the RC Cars segment, illustrated by “Mechanical DIY electric hydraulic scooter”, balancing structural strength, print fidelity and field reliability.
No FAQs for this product yet.
General safety (FusRock)
| How to route filament |
|
||
|---|---|---|---|
| Moisture control |
|
| Short breaks | Store in a sealed dry box or apply a simple vacuum pack; avoid direct sunlight. |
|---|---|
| Long-term storage | Return filament to the factory foil bag, squeeze out air (add a fresh desiccant pack if available), then place inside a household vacuum bag and pull vacuum. Keep in a cool, dry place away from sunlight. |
PTC compact dryer box: 60–70 °C for 4–6 hours.
Small lab oven (forced-air): temperature uniformity is often limited; spools can warp. Reduce temperature/time (example: 40–45 °C for ~4 hours) and cross-check the material-specific drying notes in the datasheet.
Important: if print quality does not improve, test with an empty spool before raising temperature—non-uniform heat can deform plastic flanges.
Large forced-air oven: 60–70 °C for 4–6 hours.
PS: Why do devices differ? Add an internal article or external link (“learn more”).
⚠ Read before drying
(Insert “warped vs normal” spool photos here.)
What moisture does to prints
| Dry | Damp |
|---|---|
| Cleaner surface, stable color, mechanical properties on spec | Pitting, stringing, whitening, weaker properties (material dependent) |
(Optional: 1 / 2 / 3 day exposure at ~80% RH — same test part.)
* Example photos may reference a specific grade (e.g. PAHT-CF); label yours accordingly.
No application disclaimer to display yet. Link a Product Parameters V2 record to this product in the admin.