Synced from Product Parameters V2: Basic & Appearance
| Recommended printing Condiciones | temperatura280 -- 320 ° calibre de la cubierta recomendada0.4-1.0mmsuperficie de construcción recomendada treatmentPEI or Coating with PVP glueBuild plate temperature60-80 °CChamber TempSupports printing without sealingCooling fan speedOffPrint speed30-120 mm/sRetraction distance1-3 mmRetraction speed1800-3600 mm/minRecommended Support MaterialFusFree™ S-Multi Quick-Remove SupportDrying setting100-120℃ for 4-6hAnnealing80-100℃ for 4-8h |
|---|
| Temperature280 -- 320 ° calibre recomendado del zapato 0.4-1.0mmrecomendado build surface treatmentPEI or Coating with PVP glueBuild plate temperature60-80 °CChamber TempSupports printing without sealingCooling fan speedOffPrint speed30-120 mm/sRetraction distance1-3 mmRetraction speed1800-3600 mm/minRecommended Support MaterialFusFree™ S-Multi Quick-Remove SupportDrying setting100-120℃ for 4-6hAnnealing80-100℃ for 4-8h |
consejos de impresión: Although the moisture absorption of PET material is very low, it is very sensitive to moisture. Printing after absorbing moisture will result in ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the FusForce™️ PET-CF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 100-120°C for 4-6h to restore the printing quality of FusForce™️ PET-CF.Phaetus hardened steel and above grade nozzles shall be selected, which can effectively improve the print quality. Besides, it is recommended that the thickness of the heating block should no less than 12mm.After the printing, the printed part can be annealed to further improve the strength of FusForce™️ PET-CF print part. Annealing conditions: place the printed part at 80-100°C for 4-8 hours and cool to room temperature naturally.
No matching print profile files.
Valores sincronizados desde el perfil de producto V2 vinculado; punto de partida para el slicing y pruebas de impresión.
Core temperature, speed and cooling settings from Product Parameters V2.
Nozzle, build plate and pre-print preparation recommendations.
Support material, spacing and compatible material recommendations.
FusRock 3D printing materials in the Lighting segment, illustrated by “Application: Astronomical applications—Making a reflecting telescope”, balancing structural strength, print fidelity and field reliability.
FusRock 3D printing materials in the Robotics segment, illustrated by “Robotic arm robot cable fixed protection limit sleeve”, balancing structural strength, print fidelity and field reliability.
No FAQs for this product yet.
通用安全提示（FusRock）
| 短期不使用时 | 放入密封防潮盒或进行简易抽真空即可，避免阳光直射。 |
|---|---|
| 长期不使用 | 将耗材放入出厂铝箔袋并尽量排出袋内空气（条件允许时在袋内再放一包干燥干燥剂）；外套一层家用抽真空保鲜袋后抽真空。置于阴凉干燥处，避免阳光直射。 |
PTC 小型烘干盒：60–70℃，烘干 4–6 小时。
小型恒温鼓风烘干机：箱内温度场往往不均匀，可能导致料盘变形；此类设备上建议适当降低温度并缩短单次烘干时间（示例：40–45℃，约 4 小时），并结合材料详情中的干燥建议综合判断。
重要：若按此温度烘干后打印效果仍无改善，请先用空料盘做温度测试，再酌情提高烘干温度，以防温度过高或不均匀导致料盘烘干变形。
大型恒温鼓风烘干机：60–70℃，烘干 4–6 小时。
PS：为什么不同烘干设备适用温度会有差别？可在后台插入说明或外链「点击了解」。
⚠ 操作前请阅读
（可插入「变形 vs 正常」料盘对比照片，注意控制烘干温度与摆放方式。）
耗材受潮的影响
| 未受潮 | 受潮 |
|---|---|
| 表面相对整洁、颜色正常、力学性能在规格内 | 可能出现痘痕/毛刺/拉丝、颜色发白、力学性能下降等（因材料而异） |
（可插入 RH80% 环境下拆封后第 1 / 2 / 3 天打印同一模型的对比图。）
* 上述吸湿对比示例可能因产品系列而异（例如 PAHT-CF），请在插入图片时于脚注中注明材料系列。