FusFlex™ FusFlex™ TPU90A-HF

TPU90A-HF

FusFlex™TPU90A-HF是一種易於打印的TPU材料。在相同硬度下,與其他傳統TPU耗材相比,FusFlex™TPU90A-HF更容易擠壓。當選擇合適的擠出機時,FusFlex™TPU90A-HF可以支持超過100mm/s的打印速度。
- HDT-A 热变形温度 / degC
- HDT-B 热变形温度 / degC
- 拉伸模量 / Young 模量(多状态) / MPa
- 拉伸强度(多状态) / MPa
线径1.75mm 重量1kg
线盘规格(线径/重量)
  • 规格参数
  • 配置下载
  • 打印参数
  • 相关下载
  • 应用案例
  • 常见问题
  • 健康小提示
  • 受潮处理和储存
  • 应用免责声明
  • 声明和版权
被加載材料的功能特性(與雷達對比的物性表)…< / div > < / div >
PRODUCT PARAMETERS V2

FusFlex™ TPU90A-HF

同步自产品参数管理V2:基础与外观信息

产品名称 FusFlex™ TPU90A-HF
产品型号 TPU90A-HF
适配成型方式 FDM設備使用耗材
颜色与外观 白色(White)、黑色(Black)、鲜绿色(Bright Green)
重量规格 1 kg
线径规格 1.75 mm
品牌 FusRock
供应商 FusRock

Material Properties

PropertyTesting methodTypical valueDensityISO 11831.19 g/cm³HardnessISO 761990AMelt index200°C,2.16kg22 g/10minVicat softening temperatureISO 30695°CTensile breaking strength (X-Y)ISO 52728.12±3.26 MPaelongation at break (X-Y)520±51 %tensile stress at 100% (X-Y)8.55±0.32 MPatensile stress at 200% (X-Y)10.26±0.14 MPatensile stress at 300% (X-Y)14.38±0.55 MPaSpecimens printed under the following conditions: Nozzle size 0.4mm,Nozzle temp 210°C, Bed temp 50°C, Print speed 60mm/s, Infill 100%, Infill angle ±45°Recommended printing conditions
Additional Suggestions:1.If you want to achieve high-speed printing, it is recommended to use direct extruders, such as BMG extruder, Titan extruder and Hemera extruder, and appropriately increase the nozzle temperature.2.TPU material is very easy to absorb moisture when exposed to air, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality.It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the FusFlex™ FusFlex™ TPU90A-HF vacuum foil bag for printing.Please put the unused filament back into the original aluminum foil bag for sealed storage.3.After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface.Please dry the filament in an oven at 70-80℃ for 4-6h to restore the printing quality of FusFlex™ FusFlex™ TPU90A-HF.FAQ
Most frequent questions and answersSize specifications of 1KG consumables?
DisclaimerFusrock® 3D printing filaments are suitable for general printing applications and have been tested under standard conditions.However, the performance and safety of printed products are influenced by multiple factors, including printing parameters, model design, operating environment, and intended use.By using Fusrock® materials, users acknowledge and agree to independently evaluate the suitability of printed items for their specific applications and assume all associated risks.Fusrock® shall not be held liable for any damages, injuries, or losses resulting from the practical use of products printed with its materials, including but not limited to structural failures, malfunctions, or safety hazards in operational environments.Thorough testing must be conducted before applying printed components to critical, functional, or commercial scenarios.Fusrock® products are not certified for medical, aerospace, or life-support systems, except for certifications explicitly stated by Fusrock® for specific materials.
Related ArticlesAll

Recommended printing conditions

Additional Suggestions:1.
Related ArticlesAll
FusFlex™ TPU90A-HFA 3D printed unicycle sports brace based on TPU90A
Manufacturing and R&D | Others | FusFlex™ TPU90A-HFFUSE  REALROCK FUTURE
.
  • 资料类型
  • 版本号
  • 时间
  • 操作
  • TDS
  • 1.0
  • 2025-08-01
  • 暂无匹配的打印配置文件。

    PRODUCT PARAMETERS V2

    打印参数

    以下参数同步自关联的产品参数管理V2,可作为切片与试打调参的起点。

    打印窗口

    同步自产品参数管理V2的温度、速度与冷却建议。

    喷嘴温度 210 - 240 °C
    底板温度 20 - 50 °C
    打印速度 30 - 120 mm/s
    建议喷嘴直径 0.2 - 0.2 mm

    硬件与平台

    喷嘴、底板以及打印前准备建议。

    建议底板材质 玻璃,PEI膜或PC膜

    支撑与兼容

    支撑材料、支撑间距和兼容耗材建议。

    Raft 间距 0.18 - 0.22 mm
    回抽距离 0.8 - 1.6 mm
    回抽速度 30 - 60 mm/s

    暂无收录的解决方案条目,敬请期待。

    暂无收录的常见问题,敬请期待。

    通用安全提示(FusRock)

    1. 長期大量使用 3D 打印材料時,建議在專用房間操作並保持通風。
    2. 有過敏史者請確認所用材質不會引發過敏反應。
    3. 有呼吸道慢性病者請佩戴口罩;其他人員也強烈建議操作時佩戴口罩。
    4. 對纖維類打印件進行打磨、切割等可能產生纖維逸出的操作時,請做好防護,避免刺入或吸入。
    5. 打印時請遠離兒童與嬰幼兒,注意環境安全。

    耗材(防潮)儲存要求

    短期不使用時 放入密封防潮盒或進行簡易抽真空即可,避免陽光直射。
    長期不使用 將耗材放入出廠鋁箔袋並盡量排出袋內空氣(條件允許時在袋內再放一包幹燥幹燥劑);外套一層家用抽真空保鮮袋後抽真空。置於陰涼幹燥處,避免陽光直射。
    耗材受潮處理方案及方法
    烘幹參數

    PTC 小型烘幹盒:60–70℃,烘幹 4–6 小時。

    小型恒溫鼓風烘幹機:箱內溫度場往往不均勻,可能導致料盤變形;此類設備上建議適當降低溫度並縮短單次烘幹時間(示例:40–45℃,約 4 小時),並結合材料詳情中的幹燥建議綜合判斷。

    重要:若按此溫度烘幹後打印效果仍無改善,請先用空料盤做溫度測試,再酌情提高烘幹溫度,以防溫度過高或不均勻導致料盤烘幹變形。

    大型恒溫鼓風烘幹機:60–70℃,烘幹 4–6 小時。

    PS:為什麼不同烘幹設備適用溫度會有差別?可在後臺插入說明或外鏈「點擊了解」。

    注意事項

    操作前請閱讀

    1. 沒有把握的請先用空料盤進行溫度測試,以防溫度過高或不均勻導致料盤烘幹變形。
    2. 請嚴格遵循材料詳情頁 / 材料參數管理中推薦的烘幹溫度與時間。
    3. 建議使用鼓風幹燥箱;不要讓出風口直吹料盤(避免局部過熱變形)。
    4. 烘幹時注意避開強氣流直吹線盤側面。
    5. 勿將料盤直接擱在網狀架子上(建議墊底金屬板等平整受熱面)。
    6. 取出高溫料盤時注意燙傷。
    7. 注意防火與用電安全。
    8. 盡量選用箱內溫度均勻的設備;避免使用家用微波爐等加熱嚴重不均的方式;更推薦恒溫鼓風幹燥箱類設備。

    (可插入「變形 vs 正常」料盤對比照片,注意控制烘幹溫度與擺放方式。)

    幹燥受潮對比

    耗材受潮的影響

    未受潮受潮
    表面相對整潔、顏色正常、力學性能在規格內可能出現痘痕/毛刺/拉絲、顏色發白、力學性能下降等(因材料而異)

    (可插入 RH80% 環境下拆封後第 1 / 2 / 3 天打印同一模型的對比圖。)

    * 上述吸濕對比示例可能因產品系列而異(例如 FusForce™ FusForce™ PAHT-CF),請在插入圖片時於腳注中注明材料系列。