| 推賞印刷条件 | ノズルTemperature300-340°CRecommendedノズルDiameter0.4-1.0表treatmentPEI mmRecを追加します。mmended災害軍団のコ-テ-ィングglueBuild板temperature70-80°CChamber TempSupportsファンのための印刷なんだんのですsealingCooling speedOffPrint speed30-120mm /sRetraction distance1-3 mmRetraction speed1800-3600 mm / minRecommended MaterialFusFree™s-paht quick-removeサポトをベースとしたものです。< / td > < / tr > < / body > < / table > < h3 >押し赏印刷条件< / h3 > < table class = " table < tbody > < tr > < thオリジナル> | ノズルTemperature300-340°CRecommendedノズルDiameter0.4-1.0外treatmentPEI増設定mmRecommended災害軍団のコーティングglueBuild板temperatですure70-80°sealingCooling speedOffPrint speed30-120 mm /sRetraction distance1-3mmRetraction speed1800-3600 mm / minRecommended MaterialFusFree™s-paht quick-removeはサポトをベースとしたものです。SupportDryingではsetting80 ~ 100℃で4 ~ 6、hannealing80 ~ 100℃で4 ~ 8 h < / td > < / tr > < / tbody > < / table > < h3 >印刷チップh3 > p > <印刷チップ:1ナイロンの素材は、環境内の水分を吸ってって劇場をしやすく、水分を吸ってって劇場をした後、印刷は、オザリィング、泡との連行し、し、太いいの表面の外をも目立ち、印刷の质の低下が目立ちました。印刷用のfuscoatingtm nexpa—gf25バキュームフォイル袋を开けた直后に、干燥箱(湿度15%以下)にフィラメントにをれておくことをお勧めしまはす。使用すべきは、フギラメントが元のアフロマーイホイ袋であり、返却して密封保管しておくべきはまだです。材料は、まぬれがまだ、まぬれがまだ、多くの印刷がオジング、気泡押出が太印刷面がありますです。印刷fuscoatingtm nexpa—たら25.3の品質を復元するために、80 ~ 100℃のオーブンでフィラメントを4−6時間を乾燥させてください。印刷の品質を効果に向上させることができる、硬化钢とphaetus制のグレード以上のノズルを使用することをお勧めしまはす。ま、ブロックは厚さに加熱しましたが、12mmの長さもお勧めします。印刷が終戦した後、fuscoatingtm nexpa—gf25プリント部分はアニールクリック理され、プリント部分の強度をさらに向上させることができまはす。アニ-ルの条件は、印刷部は80 ~ 100℃のオ-ブンで4−8時間を置いて、自然、室温、冷却が必要です。ですね。
一致するプリント設定ファイルはありません。
製品パラメータ V2
プリントパラメータ関連する製品パラメータ V2 の値を表示。スライシングと試作の出発点としてご利用ください。 Printing WindowCore temperature, speed and cooling settings from Product Parameters V2.
Nozzle Temperature
300 - 340 °C
Bed Temperature
70 - 80 °C
Print Speed
30 - 120 mm/s
Suggested Nozzle
0.4 - 1 mm
Hardware & PlatformNozzle, build plate and pre-print preparation recommendations.
Build Plate Material
PEI or Coating with PVP glue
Support & CompatibilitySupport material, spacing and compatible material recommendations.
Raft Gap
0.08 - 0.12 mm
Retraction
1 - 3 mm
Retraction Speed
30 - 60 mm/s
Application cases for this filament
Live listings from the Application Cases section (same taxonomy as the CMS).
1 cases
この製品の FAQ はまだ登録されていません。 通用安全提示(FusRock)
耗材(防潮)储存要求
耗材受潮处理方案及方法
烘干参数 PTC 小型烘干盒:60–70℃,烘干 4–6 小时。 小型恒温鼓风烘干机:箱内温度场往往不均匀,可能导致料盘变形;此类设备上建议适当降低温度并缩短单次烘干时间(示例:40–45℃,约 4 小时),并结合材料详情中的干燥建议综合判断。 重要:若按此温度烘干后打印效果仍无改善,请先用空料盘做温度测试,再酌情提高烘干温度,以防温度过高或不均匀导致料盘烘干变形。 大型恒温鼓风烘干机:60–70℃,烘干 4–6 小时。 PS:为什么不同烘干设备适用温度会有差别?可在后台插入说明或外链「点击了解」。 注意事项 ⚠ 操作前请阅读
(可插入「变形 vs 正常」料盘对比照片,注意控制烘干温度与摆放方式。) 干燥受潮对比 耗材受潮的影响
(可插入 RH80% 环境下拆封后第 1 / 2 / 3 天打印同一模型的对比图。) * 上述吸湿对比示例可能因产品系列而异(例如 PAHT-CF),请在插入图片时于脚注中注明材料系列。 応用免責のテキストがありません。製品にプロダクトパラメータ V2 を関連付けてください。 Copyright & Terms of Use Notice
Thank you for visiting our website! Please carefully read the following Copyright Statement and Terms of Use before using this website: Copyright Statement All content on this website, including but not limited to texts, images, graphics, audios, videos, software, as well as their compilations, codes and technical architectures (collectively referred to as the "Content"), are owned by this website or relevant right holders and protected by the Copyright Law of the People's Republic of China and other applicable laws and regulations. Without the prior written authorization of this website, no entity or individual may copy, repost, disseminate, modify, display, adapt, mirror, upload, download or otherwise use the Content of this website in any form. The copyright of any third-party content quoted on this website shall belong to the original right holders. If your legitimate rights and interests are infringed due to reasons not attributable to this website, please contact us promptly, and we will handle the matter immediately upon verification. Terms of Use You may browse, download or print the Content of this website for non-commercial purposes in compliance with relevant laws, regulations and this Notice, provided that all copyright notices and other proprietary information are retained without any modification whatsoever. Any commercial use of the Content or services of this website is strictly prohibited, including but not limited to creating derivative works based on the Content, selling or distributing the Content to third parties. It is prohibited to use automated tools (such as crawlers, robots, etc.) to obtain, copy, monitor or attempt to access the content or data of this website. Disclaimer This website endeavors to provide accurate and reliable information, but makes no express or implied warranties regarding the completeness, timeliness or accuracy of the Content. This website shall not be held legally liable for any direct or indirect losses arising from your use of the Content or services of this website. This website may contain links to third-party websites, and this website assumes no responsibility for the content and acts of any third-party websites. Rights Protection If you violate this Notice and infringe upon the legitimate rights and interests of this website, we reserve the right to pursue legal liabilities, including but not limited to filing a lawsuit or taking other legal measures. Should you have any inquiries regarding this Notice, please contact us via: [email protected] The final right of interpretation of this Notice belongs exclusively to this website. |
|---|