5% Chopped carbon fiber reinforced ABS 3D Printing Material
Product Description
FusFun™ ABS-CF is an ABS-based filament specially developed for 3D printing and it is reinforced with 5% carbon fiber. Compared with other ABS filaments, it has a much lower odor and excellent dimensional stability.
Material Properties
Property | Testing method | Typical value |
Density | ISO 1183 | 1.06 g/ cm³ |
Glass transition temperature | ISO 11357 | 101 °C |
Melt index | 250°C，2.16kg | 4 g/10min |
Vicat softening temperature | ISO 306 | 99 °C |
Determination of temperature | ISO 75：Method A ISO 75：Method B | 93 °C (1.8MPa) 98 °C (0.45MPa) |
Tensile breaking strength(X-Y) | ISO 527 | 44.97±0.46 MPa |
Elongation at break(X-Y) | ISO 527 | 2.22±0.13 % |
Young’s Modulus(X-Y) | ISO 527 | 3450.24±71.67 MPa |
Tensile breaking strength（Z） | ISO 527 | 22.30±2.75 MPa |
Young’s Modulus（Z） | ISO 527 | 2259.33±112.17 MPa |
Elongation at break（Z） | ISO 527 | 1.43±0.26 % |
Bending strength（X-Y） | ISO 178 | 75.54±2.01 MPa |
Bending Modulus（X-Y） | ISO 178 | 3261.89±49.08 MPa |
Charpy impact strength（X-Y） | ISO 179 | 7.35±0.30 KJ/㎡ |
Specimens printed under the following conditions: Nozzle size 0.4mm，Nozzle temp 250°C, Bed temp 100°C, Print speed 50mm/s, Infill 100%, Infill angle ±45°
Recommended printing conditions
Nozzle temperature | 250-270°C |
Recommended nozzle diameter | ≥0.2 mm |
Recommended build surface | Glass、PEI Film or PC Film |
Build plate temperature | 100-110 °C |
Raft separation distance | 0.16-0.18 mm |
Cooling fan speed | 0-30% |
Print speed | 30-200 mm/s |
Retraction distance | 0.4-1 mm |
Retraction speed | 1800-3600 mm/min |
Recommended Support Material | FusFree™ S-Multi Quick-Remove Support |
Printing Tips：
- Compared with PLA, PETG and other materials, ABS materials need a higher chamber temperature to help release the residual stress during the printing process. Please keep the printer chamber closed during the printing process. It can effectively avoid printed parts from warping and cracking. If the device has a heated chamber, it is recommended to set the temperature of heated chamber between 50-60°C.
- If the ABS-CF filament has been unpacked for a long time and the printing quality starts to degrade during the printing process, please dry the filament at 65-70°C for 4-6 hours before printing.
3.Although FusFun™ ABS-CF has much less odor compared with similar products, it is still recommended to place the printer in a well-ventilated area during printing.
Disclaimer
Fusrock® 3D printing filaments are suitable for general printing applications and have been tested under standard conditions. However, the performance and safety of printed products are influenced by multiple factors, including printing parameters, model design, operating environment, and intended use. By using Fusrock® materials, users acknowledge and agree to independently evaluate the suitability of printed items for their specific applications and assume all associated risks. Fusrock® shall not be held liable for any damages, injuries, or losses resulting from the practical use of products printed with its materials, including but not limited to structural failures, malfunctions, or safety hazards in operational environments. Thorough testing must be conducted before applying printed components to critical, functional, or commercial scenarios. Fusrock® products are not certified for medical, aerospace, or life-support systems, except for certifications explicitly stated by Fusrock® for specific materials.