FusFree™ S-PAHT Quick-Remove Support Material can achieve fast and easy peeling by adjusting the bonding strength to the support surface of the body material and the bonding strength of S-PAHT itself. S-PAHT Quick-Remove Support Material does not require the use of water or solvents during the removal of the support and does not produce water pollution, which is safe and environmentally friendly. It can be used in dual printhead FDM printers or 2-in/1-out FDM printers. FusFree™ S-PAHT Quick-Remove Support Material is compatible with the following FusRock® industrial grade material products. FusForce™ PAHT-GF FusForce™ PAHT-CF FusCoating™ NexPA-GF25 FusCoating™ NexPA-CF25
Product highlights
FusFree™ S-PAHT can provide a moderate bond strength to the body material through formulation and process modifications, which ensures that the body material can be molded to the support surface and can be easily separated from the support surface of the body material during removal of the support.
Product introduction
FusFree™ S-PAHT Quick-Remove Support Material can achieve fast and easy peeling by adjusting the bonding strength to the support surface of the body material and the bonding strength of S-PAHT itself. S-PAHT Quick-Remove Support Material does not require the use of water or solvents during the removal of the support and does not produce water pollution, which is safe and environmentally friendly. It can be used in dual printhead FDM printers or 2-in/1-out FDM printers. FusFree™ S-PAHT Quick-Remove Support Material is compatible with the following FusRock® industrial grade material products. FusForce™ PAHT-GF FusForce™ PAHT-CF FusCoating™ NexPA-GF25 FusCoating™ NexPA-CF25
Product details
| Parameter | Value / range |
|---|---|
| Color | Natural |
| Filament Ø | 1.75 mm |
| Net weight | 2.5 kg |
Material properties
Physical properties
| Property | Test method | Typical value |
|---|---|---|
| Density | ISO 1183 | 1.26 g/cm³ |
| Water absorption | ISO 62: Method 1 | 0.4 % |
| Melting temperature | ISO 11357 | 218 °C |
| Melt index | - | 270 g/10min |
Thermal properties
| Property | Test method | Unit | Before annealing | After annealing | After annealing, saturated moisture treatment |
|---|---|---|---|---|---|
| - | |||||