FusForce™ PC-FR
Example FDM placeholders — replace with measured TDS values.
Product highlights
Halogen-free flame retardants
FusForce™ PC-FR is an excellent flame-resistant material which is based on polycarbonate. By adding phosphorus flame retardant, PC has excellent self-extinguishing performance, and the flame-retardant grade can reach UL94 V-0 level (0.8mm). Compared with materials with halogen flame retardants, FusForce™ PC-FR will not release much smoke and toxic gases after burning. Therefore, FusForce™ PC-FR is safer and more environmentally friendly, while still maintaining the excellent mechanical properties and heat resistance of polycarbonate.
Product introduction
-
Product details
| Parameter | Value / range |
|---|---|
| Color | Black |
| Filament Ø | 1.75 mm |
| Net weight | 2.5 kg |
Material properties
Physical properties
| Property | Test method | Typical value |
|---|---|---|
| Density | ISO 1183 | 1.19 g/cm³ |
| Melt index | - | 250 g/10min |
Thermal properties
| Property | Test method | Unit | 102°C (1.8MPa) | 107°C (0.45MPa) | 106°C (1.8MPa) | 110°C (0.45MPa) |
|---|---|---|---|---|---|---|
| - | ||||||
Mechanical properties
| Property | Test method | Unit | 102°C (1.8MPa) | 107°C (0.45MPa) | 106°C (1.8MPa) | 110°C (0.45MPa) |
|---|---|---|---|---|---|---|
| Tensile Yield Strength XY | ISO 527 | MPa | 58.09 ± 0.68 | 61.50 ± 0.66 | - | - |
| Tensile Modulus XY | ISO527 | MPa | 2754.86 ± 61.29 | - | - | 50.28 ± 0.94 |
| Elongation at Break XY | ISO527 | % | 5.06 ± 0.75 | - | - | 527 |
| Flexural Strength XY | ISO178 | MPa | 83.99 ± 0.76 | 90.73 ± 0.35 | - | - |
| Notched Impact XY | ISO179 | kJ/m² | 13.43 ± 1.26 | 9.49 ± 0.76 | - | - |
| Tensile Modulus Z | ISO527 | MPa | 2462.30 ± 224.55 | - | - | 2.65 ± 0.21 |
Printed specimen parameters:试样打印参数：喷嘴大小0.4mm，喷嘴温度255°C，底板加热110°C，腔体温度55℃，打印速度50mm/s，填充率100%，填充角度±45°