FusFun™ ToughPETG-HF
Example FDM placeholders — replace with measured TDS values.
Product highlights
High Impact Resistance
FusRock® has improved the notch impact strength of FusFun™ ToughPETG-HF to more than twice that of ordinary PETG without affecting the interlayer bonding strength in the Z-axis direction through toughness improvement technology.
High Speed Printability
FusFun™ ToughPETG-HF has excellent material flow and good modeling effect, which can achieve perfect printing results in most printers. The max printing speed is close to 400mm/s.
产品规格
Product introduction
-
Product details
| Parameter | Value / range |
|---|---|
| Color | -, -, -, -, -, -, -, - |
| Filament Ø | 1.75 mm |
| Net weight | 1 kg |
Material properties
Physical properties
| Property | Test method | Typical value |
|---|---|---|
| Density | ISO 1183 | 1.27 g/cm³ |
| Melt index | - | 220 g/10min |
| Glass transition temperature | ISO 11357 | 80 °C |
Thermal properties
| Property | Test method | Unit | Typical value |
|---|---|---|---|
| - | |||
Mechanical properties
| Property | Test method | Unit | Typical value |
|---|---|---|---|
| Tensile Modulus XY | ISO527 | MPa | 1821.82 ± 49.41 |
| Tensile Break Strength XY | ISO527 | MPa | 21.92 ± 3.98 |
| Elongation at Break XY | ISO527 | % | 14.04 ± 7.77 |
| Flexural Strength XY | ISO178 | MPa | 71.40 ± 0.74 |
| Flexural Modulus XY | ISO178 | MPa | 1895.07 ± 36.19 |
| Notched Impact XY | ISO179 | kJ/m² | 16.39 ± 2.16 |
| Tensile Strength Z | ISO527 | MPa | 42.70 ± 0.51 |
| Tensile Modulus Z | ISO527 | MPa | 1955.67 ± 179.30 |
| Elongation at Break Z | ISO527 | % | 4.51 ± 0.82 |
Printed specimen parameters:Specimens printed under the following conditions: Nozzle size 0.4mm，Nozzle temp 240°C, Bed temp 80°C, Print speed 45mm/s,