PET-CF专为FDM 3D打印工艺开发，基材选用PET工程材料，具有低吸湿，高强度，耐蠕变，耐溶剂和高耐热性的特点。打印过程中尺寸稳定性好，无翘边，无收缩现象，无气味，无需环境保温。并且可以与FusFree™ S-Multi易剥离支撑材料配合使用，解决复杂模型支撑面成型效果差的难题。
Produkthighlights
Smart Fiber Reinforced Technology
FusRock® controlling the dispersion and distribution of chopped carbon fibers within the material matrix during the extrusion process, the fibers form a mesh skeleton structure within the material and bear most of the load transferred by the material matrix. Smart Fiber Reinforced Technology greatly improves the mechanical properties and heat resistance of the material, and releases the internal stress during the printing process through the fiber mesh structure, resulting in good dimensional stability of the printed part and no warpage.
Low creep
The molecular chain structure of PET is highly regular and has a rigid benzene ring structure, so that PET has better mechanical properties and less deformation under long-term load. Compared with PA and PC materials, PET has better creep-resistance.
Produktvorstellung
PET-CF专为FDM 3D打印工艺开发，基材选用PET工程材料，具有低吸湿，高强度，耐蠕变，耐溶剂和高耐热性的特点。打印过程中尺寸稳定性好，无翘边，无收缩现象，无气味，无需环境保温。并且可以与FusFree™ S-Multi易剥离支撑材料配合使用，解决复杂模型支撑面成型效果差的难题。
Produktdetails
| Parameter | Wert / Bereich |
|---|---|
| Color | Black |
| Filament Ø | 1.75 mm |
| Nettogewicht | 2.5 / 3 kg |
Materialeigenschaften
Physikalische Eigenschaften
| Eigenschaft | Prüfmethode | Typischer Wert |
|---|---|---|
| 密度 | ISO 1183 | 1.30 g/cm³ |
| 吸湿率 | ISO 62: Method 1 | 0.5 % |
| 熔点 | ISO 11357 | 251 °C |
| 熔融指数 | - | 270 g/10min |
Thermische Eigenschaften
| Eigenschaft | Prüfmethode | Einheit | 未退火 | 退火后 | 退火后饱吸湿处理 |
|---|---|---|---|---|---|
| 热变形温度 A | ISO 75: Method A (1.80 MPa) | °C | 76.6 | 115.6 | 105.4 |
| 热变形温度 B | ISO 75: Method B (0.45 MPa) | °C | 86.7 | 175.4 | 174.5 |
Mechanische Eigenschaften
| Eigenschaft | Prüfmethode | Einheit | 未退火 | 退火后 | 退火后饱吸湿处理 |
|---|---|---|---|---|---|
| 拉伸强度 XY | ISO527 | MPa | 72.51 ± 1.39 | 70.82 ± 2.74 | 67.97 ± 2.64 |
| 拉伸模量 XY | ISO527 | MPa | 5730.88 ± 200.63 | 6208.45 ± 462.92 | 6227.90 ± 543.32 |
| 断裂伸长率 XY | ISO527 | % | 2.49 ± 0.22 | 1.46 ± 0.10 | 1.47 ± 0.10 |
| 弯曲强度 XY | ISO178 | MPa | 114.47 ± 1.89 | 110.79 ± 3.36 | 108.47 ± 3.72 |
| 弯曲模量 XY | ISO178 | MPa | 5345.71 ± 231.24 | 5588.24 ± 363.94 | 5669.56 ± 333.24 |
| 缺口冲击 XY | ISO179 | kJ/m² | 7.75 ± 1.08 | 4.59 ± 0.15 | 4.30 ± 0.28 |
| 拉伸强度 Z | ISO527 | MPa | 34.13 ± 0.93 | - | - |
| 拉伸模量 Z | ISO527 | MPa | 3270.44 ± 62.77 | - | - |
| 断裂伸长率 Z | ISO527 | % | 1.20 ± 0.04 | - | - |
Druckparameter der Probe:试样打印参数：喷嘴温度320°C，底板加热80°C，打印速度45mm/s，填充率100%，填充角度±45°
Haftungsausschluss
Fusrock® 3D 打印耗材适用于通用打印用途，已在标准条件下进行测试。然而，打印成品的性能与安全性受多种因素影响，包括打印参数、模型设计、使用环境及实际用途。使用 Fusrock® 材料即表示用户已知悉并同意，自行评估打印件是否适用于其具体应用，并承担由此产生的全部风险。Fusrock® 对使用本公司耗材打印的产品在实际应用中可能导致的任何损害、伤害或损失不承担任何责任，包括但不限于结构失效、功能异常或使用环境中的安全隐患。在将打印件应用于关键、功能性或商业性场景前，请务必进行充分测试。除Fusrock®已标明材料所获得的各项认证资质外，Fusrock® 产品未取得医疗、航天或生命支持系统认证资质。